Investigation of the SiN Deposition and effect of the hydrogenation on solid-phase crystallisation of evaporated thin-film silicon solar cells on glass

Abstract

One of the poly-Si thin-film cells developed at the University of New South Wales (UNSW) is the EVA cell. In this work, SiN films for EVA cells as an antireflection/barrier coating were investigated. In addition, the effect of hydrogenation pre-treatment of solid phase crystallisation (SPC) on grain size and open-circuit voltage (Voc) was investigated. The SiN films deposited by PECVD were examined for uniformity of the thickness and the refractive index of the films across the position of the samples in the PECVD deposition system. A spectrophotometric analysis was used to determine these film properties. It was found that these properties were very uniform over the deposition area. Good repeatability of the depositions was also observed. A series of SiN film depositions by reactive sputtering were also performed to optimize the deposition process. Parameters adjusted during the deposition were nitrogen flow rate, substrate bias, and substrate temperature. By investigating the deposition rate, refractive index, and surface roughness of the films, the three deposition parameters were optimised. The effects of post SiN deposition treatments (a-Si deposition, SPC, RTA, and hydrogenation) on thickness and refractive index of both SiN films deposited by PECVD and reactive sputtering were investigated by using samples which have the same structure as the EVA cells. The thickness of the PECVD SiN films decreased about 6 % after all the treatments. On the other hand, the thickness reductions of the reactively sputtered SiN films were very small. The refractive index of the PECVD SiN films increased about 0.6 % after the treatments, whereas that of the reactively sputtered SiN films decreased 1.3 % after the treatments. As a possible method to improve the performance of EVA cells, hydrogenation of a-Si was investigated as a pre-treatment of SPC process. There were no obvious differences in the grainsize and the Voc of the EVA cells with and without the hydrogenation. Therefore it is likely that the hydrogenation pre-treatment of SPC does not have a beneficial effect on the performance of EVA cells.