Abstract
The high stiffness to weight ratio and fatigue resistance make carbon fibre composites suitable for both military and large civil aircraft. The limited ability of current numerical methods to capture the complex growth of damage in laminated composites leads to a conservative design approach applied in today's composite aircraft structures. The aim of the presented research was to develop an improved methodology for the failure prediction of laminated composites containing delaminations located between arbitrary layers in the laminate, and to extend the investigations to composite structures subjected to barely visible impact damage (BVID).
The advantages of fracture mechanics-based methodologies to predict interlaminar failure in composite structures were identified, from which the crack tip element (CTE) approach and the virtual crack closure technique (VCCT) were selected for assessment. Extensive validation of these fracture mechanics methods is presented on a number of composite structures ranging from coupons to large stiffened panels. It was shown that the VCCT was relatively insensitive to the crack front mesh size, whilst predictions using the CTE methodology were significantly influenced by the element size. Based on the obtained results modelling guidelines for the VCCT and CTE were established.
Significant contribution of this research to the field of the analysis of composite structures was the development of a novel test method for the evaluation of embedded single and multi-level delaminations. The test procedure of the single delamination specimen was proposed as an analogous test to conventional compression experiments. The transverse test overcame the inherent problems of in-plane compression testing and produced less scatter of experimental measurements. Quantitative analysis of numerical results employing the validated finite element modelling approaches showed that the failure load and location were in agreement with experiments. Furthermore, new modelling techniques for composite structures containing BVID proposed in this research produced good correlation with test data from the compression after impact (CAI) test. The study of BVID provided a significant contribution toward the knowledge of the applicability of implicit FE solvers to predict failure of CAI specimens as well as the criticality of centrally impacted specimens.