Growth, Properties, and Applications of Transition Metal Dichalcogenide Nanocrystals

Access & Terms of Use
embargoed access
Embargoed until 2024-11-09
Copyright: Wang, Shuangyue
Two-dimensional transition metal dichalcogenide (TMD) nanocrystals (NCs) exhibit unique optical and electrocatalytic properties. However, the growth of uniform and high-quality NCs of monolayer TMD remains a challenge. Until now, most of them are synthesized via solution-based hydrothermal process or ultrasonic exfoliation method, in which the capping ligands introduced from organic solution often quench the optical and electrocatalytic properties of TMD NCs. Moreover, it is difficult to homogeneously disperse the solution-based TMD NCs on a substrate for device fabrication since the dispersed NCs can easily aggregate. Here, we put forward a novel CVD method to grow closely-spaced TMD NCs and explored the growth mechanism and attempts on the size control. Their applications acting as electrocatalysts and adhesion layer for Au film deposition have been also well displayed. Through the whole chapters of this thesis, the following aspects are highlighted: 1. MoS2 and other TMD nanocrystals have been grown on the c-plane sapphire. The surface oxygen vacancies determine the density of TMD nanocrystals. The MoS2 nanocrystals demonstrate excellent hydrogen evolution reaction and surface-enhanced Raman scattering performance owing to the abundant edges. 2. Deep insights into the growth of MoS2 nanograins have been explored. The surface step edges and lattice structures of the underlying sapphire substrates have a significant influence on the growth behaviors. The step edges could modulate the aggregation of MoS2 nanograins to form unidirectional triangular islands. The Raman spectra of MoS2 demonstrate a linear relationship with the crystal size of MoS2. 3. The orientation of sapphire substrate has an of importance effect on the critical size of MoS2 nanocrystals. The MoS2 nanocrystals have the smallest size on the r-plane sapphire, besides, the MoS2 on r-plane sapphire demonstrates the sintering-resistance feature, which is attributed to the edge-pinning effect when MoS2 edges are anchored on the sapphire surface. 4. The MoS2 nanocrystalline layer was utilized as the adhesion layer for Au film depositing on a sapphire substrate. The Au films on MoS2 displayed superior transmittance and electrical conductivity as well as outstanding thermal stability, which lay in the strong binding of Au film with MoS2 nanocrystalline layer.
Persistent link to this record
Link to Publisher Version
Link to Open Access Version
Additional Link
Conference Proceedings Editor(s)
Other Contributor(s)
Corporate/Industry Contributor(s)
Publication Year
Resource Type
Degree Type
PhD Doctorate
UNSW Faculty